                    微钠白刚玉微粉

                            微钠白刚玉微粉简介

                    Introduction of low-sodium white corundum micropowders



                    经过五年多的研发,我公司已能批量生产微钠白刚玉块、段砂、粒度号砂、磨粉、微钠白刚玉微粉等。

                    After 5 years of research and development, Zhengzhou Yufa Abrasive Co.Ltd has already mastered the technology of producing low-sodium white corundum block,  section corundum sand, grain corundum sand, grinding powders, and low-sodium oxide white corundum micropowders in quantity.

                     

                    微钠白刚玉微粉是由我公司生产的微钠白刚玉块经深度精加工而成。

                    Low-sodium white corundum micropowder are carefully manufactured from the low-sodium white corundum blocks made by ourselves.

                     

                    微钠白刚玉是指:含氧化钠量在0.010.09%之间的白刚玉。它的原料是经过深加工的氧化铝。微钠白刚玉是白刚玉中一种含氧化钠量较低的产品。普通白刚玉中的氧化钠含量在0.2—0.6%之间。

                    Low-sodium white corundum indicates the white corundum in which the content of sodium oxide is between 0.01-0.09%, and the raw material of which is   alumina processed in depth . Low-sodium white corundum is a type of low sodium-content product. By contrast, the sodium content in the common white corundum is between 0.2%—0.6 .

                     

                    微钠白刚玉的主相是α-Al2O3。

                    The main phase of the low-sodium white corundum is α-Al2O3.

                     

                    氧化钠对于白刚玉是一种有害杂质,它与氧化铝在熔融状态下生成β-Al2O3,生成量随氧化钠含量的增加而增大。β-Al2O3的熔点低,体密低,硬度低。白刚玉中的Na2O主要以Na2O·11AL2O3(β-Al2O3)的形式出现,如果氧化铝原料中含有0.6%以上的氧化钠,利用它生产的白刚玉中就会含百分之十以上的β-Al2O3

                    Sodium oxide is a harmful impurity in white corundum. It can react chemically with alumina in melting state and generate β-Al2O3 . The higher the sodium oxide content is, the more the β-Al2O3 forms. β-Al2O3 is featured with low melting point, low bulk density, and low hardness. The sodium oxide is coming in the form of Na2O·11AL2O3(β-Al2O3). If the sodium oxide content in alumina is higher than 0.6%, the β-Al2O3 content in the produced white corundum will be higher than 10% .

                     

                    β-Al2O3α-Al2O3相比有三低,一是熔点低,二是密度低,三是硬度低,具体如下表所示。                                                              

                    Compared to α-Al2O3,β-Al2O3 has lower melting point, lower density, and lower hardness, as shown in the following table.


                    名称Phase

                    化学成份

                    Chemical compositions

                    晶系

                    Crystal system

                    密度

                    Density

                    (g/cm3

                    显微硬度

                    Micro hardness

                    (Kg/mm2)

                    熔点Melting point

                    ()

                    α-Al2O3

                    Al2O3

                    六方

                    Hexagonal

                    4.0

                    2300

                    2050

                    β-Al2O3

                    Na2O·11Al2O3

                    三方

                     Trigonal

                    3.24

                    1300~1600

                    1600














                    我公司生产的微钠白刚玉α相率可达98%以上。

                    The α-Al2O3 content of the low-sodium oxide white corundum produced by Yufa is higher than 98%.

                    下表所示是我公司为某单位生产的微钠白刚玉1-0段砂的化学成份

                    The following table shows the chemical compositions of the low-sodium oxide white corundum 1-0 section sand for a customer.

                    报告编号

                    Report No.

                    Na2O%

                    SiO2%

                    Fe2O3%

                    Al2O3%

                     

                     

                     

                     

                    2013-06-693

                    0.01

                    0.034

                    0.012

                    99.84

                    下表所示是我公司为某单位生产的微钠白刚玉块的化学成份

                    The following table shows the chemical compositions of the low-sodium oxide white corundum block for a customer.

                    报告编号

                    Report No.

                    Na2O%

                    SiO2%

                    Fe2O3%

                    Al2O3%

                    减%

                    LOI

                     

                     

                    2009-04-134

                    0.06

                    0.02

                    0.02

                    99.84

                    0.06

                    下表所示是我公司为某单位生产的微钠白刚玉325#粉的化学成份

                    The following table shows the chemical compositions of the low-sodium oxide white corundum 325 powder for a customer.

                    报告编号

                    Report No.

                    Na2O%

                    SiO2%

                    Fe2O3%

                    Al2O3%

                    减%

                    LOI

                     

                    2009-12-855

                    ,0.02;

                    0.05

                    0.02

                    99.82

                    0.09

                    下表中所示我公司为某位生产的微钠白刚玉10段砂的化学成份

                    The following table shows the chemical compositions of the low-sodium oxide white corundum 1-0 section sand for a customer.

                    报告编号

                    Report No.

                    Na2O%

                    SiO2%

                    Fe2O3%

                    Al2O3%

                    减%LOI



                    2009-12-886

                    0.02

                    0.04

                    0.03

                    99.79

                    0.12